POE compound:
It is the Poly Olefin Elastomer (POE) of a copolymer of ethylene acten produced using solution polymerization making use of the catalyst of metalson. This product is mainly used as impact modifier in various compounds. This material is mainly used in compounds of car shields. It may however be used in different industries such as compounds used in producing pipes etc.
Application:
- Production of pipes
- Production of automotive parts
Technical specifications of the product are as follows:
| Typical Properties |
Values |
Units |
Methods |
| Physical |
|
|
|
| Melt Flow Rate (230 °C, 2.16 kg) |
2.0 |
gr/10min |
ASTM D1238 |
| Density |
0.868 |
gr/cm^3 |
ASTM D 792 |
| Mechanical |
|
|
|
| Tensile Properties |
|
|
|
| Stress at Break |
9.3 |
MPa |
ASTM D638 |
| Elongation |
50 |
% |
ASTM D638 |
| Modulus |
2.9 |
MPa |
ASTM D638 |
| Durometer Hardness |
|
|
|
| Shore A (1 second) |
71 |
- |
ASTM D2240 |
| Shore B (1 second) |
21 |
- |
ASTM D2240 |
| Flexural Modulus (1% Secant) |
13.2 |
MPa |
ASTM D790 A |
| Tear Strength (Type C) |
39.2 |
KN/m |
ASTM D624 |
| Thermal |
|
|
|
|
| Peak Melting Temperature |
62 |
°C |
SABIC Method |
| Glass Transition Temperature, Tg |
-52 |
°C |
SABIC Method |